1. Company Profile
Since its inception in October 2010, BAYGOLD COMMERCIAL(QINGDAO)CO., LTD has rapidly risen to become a trailblazer in the industry, recognized as a leading enterprise driving innovation and excellence.
With a steadfast commitment to advancing rubber technology, BAYGOLD is synonymous with cutting-edge innovation and unparalleled quality.
BAYGOLD has grown into a comprehensive powerhouse specializing in tire design and the production of tire wire, tire cord fabric, rubber chemicals, and essential tire materials. By 2018, the Group's remarkable annual output included 10,000 tons of rubberized tire cord, 15,000 tons of tire wire, and 30,000 tons of fabric.
(This encompasses tire cord fabric, chafer fabric, conveyor fabric, and tire liner fabric)While expanding aggressively in domestic markets, the Group also explores international markets with vigor. Our products are now exported to over 100 countries, including Europe, America, the Middle East, Africa, and Southeast Asia. With unmatched quality and comprehensive after-sales service, the company has earned trust and acclaim from customers worldwide.
Renowned globally, BAYGOLD COMMERCIAL(QINGDAO)CO., LTD continues to accelerate its development and enhance customer service. To further this mission, Baygold Group has invested in an expansive 6,000 square meters of warehouse space for logistics and storage operations. This strategic move positions Baygold Group as a leading comprehensive enterprise, seamlessly integrating production, technical research, and industry trade.
With ambitions to become a multifaceted enterprise group that integrates production, technical research, and pioneering solutions, Baygold Group remains unwavering in its dedication to brand development through duty and loyalty.
Baygold Group is steadfast in its commitment to brand development, pledging to go above and beyond in serving our customers and ensuring their utmost satisfaction.
2. Technical Specification
5. Our Clients
6. Why Choose Us
Company Profile
Baygold Group specializes in the manufacture and export of tire and rubber hose framework materials for the global industrial sector.
With a decade of expertise in framework materials, we stand as professionals in the field.
Our product range includes:
Tyre cord fabric for tires and fishing nets,
EE/EP/NN fabric for conveyor belts,
Liner fabric for tires,
Filter fabric for
Various industries,
Bead wire for tires and hoses,
Steel cord for tires,
Rubberized tire cord fabric for tires and hoses,
Rubberized steel cord for tires and hoses.
Our products are supplied to all major tire factories in China and exported to Southeast Asia, Africa, Europe, South America, and beyond.
We uphold a commitment to quality first, a customer-centric focus, and a win-win policy.
We earnestly look forward to cooperating with you.
Product Description
Dipped tire cord fabric
Primarily crafted from nylon 6, nylon 66, and polyester, it offers:
1. High breaking strength,
2. Excellent impact resistance,
3. Superior fatigue-proof strength,
4. Boasts impressive adhesive strength with rubber, ensuring superior performance and durability.
This premium-grade skeleton material stands as an indispensable component for a myriad of rubber products, offering unmatched durability and support.
It plays a pivotal role in maintaining shape and bearing loads with unwavering reliability and strength.
Exceptional Features
Superior breaking strength, ensuring long-lasting durability,
Outstanding anti-fatigue strength, ideal for high-stress applications,
Remarkable impact resistance, providing excellent protection against physical stresses,
Excellent bearing performance, enhancing the overall lifespan of the product.
Strong adhesive strength with rubber, ensuring a secure and lasting bond.
Versatile Usage
Widely used for robust reinforcement in:
Rubber tires, adding strength and durability,
Conveyor belts, ensuring longevity and reliability,
Rubber hoses, providing enhanced resistance to wear and tear,
Flexible oil tanks for industrial applications, guaranteeing flexibility and durability.
Packing and Delivery Details:
1. Packing Details: Conforms to international standards for export packing, either in packages or customized as per customer's requirements.
The fabric is meticulously wound on a wooden or iron shaft, enclosed by a layer of black polyethylene film, then covered with PE film, and finally secured with a tightly woven PP bag for utmost protection.
Each roll's weight and length can be customized to meet specific customer specifications, ensuring the perfect fit.
2. Payment Terms: 100% L/C at sight, or 30% T/T in advance with the remaining 70% upon sight of B/L copy, providing flexible options for our customers.
3. Delivery Timeframe:
Upon receipt of a workable deposit:
2-5 days for sample production, ensuring quick availability for assessment,
15-20 days for 1-3 20 FCL containers, offering timely delivery for bulk orders,
20-30 days for 3-5 20 FCL containers, accommodating larger order volumes efficiently.
4. Sample Policy:
Samples are provided free of charge, allowing you to evaluate quality risk-free.
For express costs exceeding 15 USD, please provide your DHL, ***, EMS, etc., account number for freight collection, ensuring smooth and convenient delivery.
7. Technical Specification
| Cord Construction |
Unit |
700Dtex/1
(630D/1) |
930Dtex/1
(840D/1) |
1400Dtex/1
(1260D/1) |
1870Dtex/1
(1680D/1) |
700Dtex/2
(630D/2) |
930Dtex/2
(840D/2) |
1400Dtex/2
(1260D/2) |
1870Dtex/2
(1680D/2) |
2100Dtex/2
(1890D/2) |
1400Dtex/3
(1260D/3) |
1870Dtex/3
(1680D/3) |
2100Dtex/3
(1890D/3) |
| Tensile Strength |
N |
≥50 |
≥70 |
≥107 |
≥137 |
≥107.0 |
≥137.2 |
≥215.6 |
≥279.3 |
≥313.6 |
≥313.6 |
415 |
≥460 |
| Elongation |
|
|
|
|
|
|
|
|
|
|
|
|
|
| At 150N(15.3KG) |
|
|
|
|
|
|
|
|
|
|
|
|
9.5±0.8 |
9.5±0.8 |
| At 100N(10.2KG) |
% |
|
|
|
|
|
|
|
|
8.0±0.8 |
8.0±0.8 |
|
|
| At 88.2N(9KG) |
% |
|
|
|
|
|
|
|
8.0±0.8 |
|
|
|
|
| At 66.6N (6.8KG) |
% |
|
|
|
|
|
|
8.0±0.8 |
|
|
|
|
|
| At 44.1 N (4.5KG) |
% |
|
11.0±1.0 |
|
8.0±0.8 |
|
8.0±0.8 |
|
|
|
|
|
|
| At 33N (3.4KG) |
% |
|
|
8.0±0.8 |
|
8±0.8 |
|
|
|
|
|
|
|
| At 28N (2.9KG) |
% |
|
|
|
|
|
|
|
|
|
|
|
|
| At 22.6N (2.3KG) |
% |
|
7.5.±0.8 |
|
|
|
|
|
|
|
|
|
|
| At 17N (1.7KG) |
% |
7.5.±0.8 |
|
|
|
|
|
|
|
|
|
|
|
| Adhesion(H-Test) |
N/CM |
≥43 |
≥54 |
≥70 |
≥83.0 |
≥95 |
≥117.6 |
≥147 |
≥166.6 |
≥176.4 |
≥176.4 |
≥235 |
≥255 |
| Cord Guage |
MM |
|
0.32±0.03 |
0.39±0.03 |
0.45±0.03 |
|
0.53±0.03 |
0.65±0.03 |
0.75±0.03 |
0.78±0.03 |
0.78±0.03 |
0.92±0.03 |
0.96±0.03 |
| Dip Pick Up |
% |
4.2±1.0 |
4.2±1.0 |
4.2±1.0 |
4.2±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
4.5±1.0 |
| Elongation at Break |
% |
|
20±2 |
20±2 |
20±2 |
|
≥18 |
≥19 |
≥20 |
≥21 |
≥21 |
≥23 |
≥24 |
| Moisture Content |
% |
≤1.5 |
≤1.5 |
≤1.5 |
≤1.5 |
≤1.5 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
Heat Shrinkage
(160ºC,2Min) |
% |
≤4.5 |
≤4.5 |
≤5 |
≤5 |
≤6.5 |
≤6.5 |
≤7.0 |
≤7.0 |
≤7.0 |
≤7.0 |
≤6.5 |
≤6.5 |
| Twist |
PLY |
T/M |
260±15 |
210±15 |
190±10 |
160±10 |
460±15 |
|
|
|
|
320±15 |
240±15 |
240±15 |
| Cable |
|
|
|
|
|
460±15 |
370±15 |
330±15 |
320±15 |
320±15 |
240±15 |
240±15 |
| Fabric Width |
CM |
|
CM±1 |
CM±1 |
CM±1 |
|
CM±1 |
CM±1 |
CM±1 |
CM±1 |
CM±1 |
|
|
| Roll Length |
M |
|
2000/3000 |
1080 |
1080 |
|
1200 |
1200 |
1350 |
900 |
900 |
|
|
| Weft Density |
END/10CM |
|
8--10 |
8--10 |
8--10 |
|
8--10 |
8--10 |
8--10 |
8--10 |
8--10 |
|
|
| OTHER SIZES AND SPECIAL REQUIREMENTS CAN BE MUTUALLY NEGOTIATED FOR CONFIRMATION |
|
|
|
| Fabric Properties |
UNIT |
210D/1 multifilament X |
420D/1 multifilament X |
|
| 210D/1 multifilament |
420D/1 multifilament |
420D1 PIRELLI |
| Content |
|
Nylon 6/ Nylon 66 |
Nylon 6/ Nylon 66 |
|
| Cord Gauge |
|
0.15±0.02 |
0.24±0.03 |
0.23±0.05 |
| Warp Density |
Ends/10CM |
415 |
236 |
236±5 |
| Warp Breaking Load |
N/END |
≥13 |
≥30 |
≥34.3 |
Warp Elongation at
22.1N break |
% |
|
|
11±2 |
| Warp Elongation at break |
% |
20±3 |
20±3 |
22±4 |
| Dip Pick Up |
% |
|
|
4.5±1 |
| Adhesion |
N/END |
≥13 |
≥20 |
≥29.4 |
| Water Content |
% |
≤1.5 |
≤1.5 |
≤1.0 |
Shrinkage in hot air
30min@150ºC |
% |
≤5 |
≤5 |
≤5 |
| Warp Twist |
TM |
|
280±20 |
280±20 |
| OTHER SIZES AND SPECIAL REQUIREMENTS CAN BE MUTUALLY NEGOTIATED FOR CONFIRMATION |
|
| Cord Construction |
Unit |
1100Dtex/2
(1000D/2) |
1100Dtex/3
(1000D/3) |
1440Dtex/2
(1300D/2) |
1440Dtex/3
(1300D/3) |
1670Dtex/2
(1500D/2) |
1670Dtex/3
(1500D/3) |
2200Dtex/2
(2000D/3) |
2500Dtex/2
(2250D/2) |
| Tensile Strength |
N |
≥137 |
≥202 |
≥178 |
≥260 |
≥202 |
≥305 |
≥270 |
≥305 |
| Elongation |
|
|
|
|
|
|
|
|
|
| At 44.1N(4.5KG) |
% |
4.6±1.0 |
|
|
|
|
|
|
|
| 66.6N(6.8KG) |
% |
|
4.6±1.0 |
4.6±1.0 |
|
4.6±1.0 |
|
|
|
| 88.2N(9KG) |
% |
|
|
|
4.6±1.0 |
|
|
4.6±1.0 |
|
| 100N (10KG) |
% |
|
|
|
|
|
4.6±1.0 |
|
4.6±1.0 |
| Adhesion(H-Test) |
N/CM |
≥125 |
≥138 |
≥127 |
≥147 |
≥138 |
≥160 |
≥170 |
≥180 |
| Cord gauge |
MM |
0.56±0.03 |
0.66±0.03 |
0.61±0.03 |
0.74±0.03 |
0.66±0.03 |
0.81±0.03 |
0.77±0.03 |
0.80±0.03 |
| Dip pick up |
% |
3+1 |
3+1 |
3+1 |
3+1 |
3+1 |
3+1 |
3+1 |
3+1 |
Elongation
at break |
Normal |
% |
≥13 |
≥13 |
≥13 |
≥13 |
≥13 |
≥13 |
≥13 |
≥13 |
| HMLS |
% |
≥11 |
≥11 |
≥11 |
≥11 |
≥11 |
≥11 |
≥11 |
≥11 |
| Moisture Content |
% |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
≤1.0 |
Heat Shrinkage
(177ºC×2min) ≤ |
% |
HMLS fabric ≤ 2.5,Normal fabric≤ 3.5 |
| OTHER SIZES AND SPECIAL REQUIREMENTS CAN BE MUTUALLY NEGOTIATED FOR CONFIRMATION |